Abstract
Single-crystal superalloys have been popularly employed in high-temperature parts of gas turbines, such as blades. However, the welds of such alloys are highly susceptible to solidification cracking, which limits their applicability to high-temperature turbine blades. In this study, the effects of characteristics of weld solidification on solidification cracking susceptibilities (solidification..... More

Abstract
This study analyzed a recrystallization phenomenon that occurred simultaneously with hightemperature oxidation on the surface of a directionally solidified CM247LC creep specimen, using optical and scanning electron microscopy. After heat treatment, the surface of the specimen subjected to the creep test at 982oC was oxidized by exposure to high temperature..... More

Abstract
The efficiency of gas turbines depends on the gas turbine working temperature. Single crystal blades are being applied more often than equiaxed blades in gas turbine engines, to increase the turbine inlet temperature, resulting in enhanced turbine engine efficiency. Single crystal blades endure creep conditions at high temperature better than..... More

Abstract
In this study, the liquation cracking temperature range (LCTR) of over-aged 247LC superalloy repair welds was quantitatively evaluated using spot-Varestraint testing, especially for application in the repair weld heat-affected zone (HAZ). The metallurgical mechanism of the evaluated liquation cracking susceptibility and variation of the LCTRs of the over-aged 247LC superalloys..... More

Abstract
The influence of trace amounts of sulfur (S) on the microstructural evolution, tensile and creep properties in directionally solidified (DS) Ni-based superalloy GTD-111 were systematically investigated. Doping of S in the range of < 1 to 154 ppm resulted in the formation of a Ti₂SC-type carbosulfide phase near the coarse..... More

Abstract
In this study, the liquation cracking susceptibility in the heat-affected zone of CM247LC superalloy gas turbine blades during repair welding was quantitatively evaluated using a newly developed pre-weld Varestraint test method. The repair welding geometry was replicated through Varestraint tests for the pre-weld bead. The liquation cracking susceptibility, that is,..... More

Abstract
The metallurgical aspects of weld solidification cracking in Ni-based superalloys (with Ti+Al > 5 mass%) have not been widely investigated thus far. Herein, the solidification cracking susceptibility of the CM247LC superalloy and its welds with ERNiFeCr-2 filler wire was quantitatively evaluated using a novel modified Varestraint testing method, for the..... More

Abstract
The metallurgical aspects of weld cracking in Ni-based superalloys remain relatively unexplored in existing research. The present study performed comprehensive metallurgical and manufactural investigations into the weldability of an Ni-based superalloy, CM247LC, from the viewpoint of the liquation cracking behavior and its susceptibility. Metallurgical solutions to suppress the liquation-cracking susceptibility..... More

Abstract
In this study, the weldability of the as-cast CM247LC superalloy for turbine blade applications was metallurgically evaluated in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc welding was performed at the tip..... More

Abstract
The effect of aging heat treatment conditions on the mechanical properties and microstructure of the base and weld metal of Alloy 282 superalloy was investigated. The aging heat treatment conditions employed in this study were as follows: two-steps (1010 °C for 2 hours plus 788 °C for 8 hours) and..... More

Abstract
The hot crack resistance and mechanical properties of flux cored arc (FCA) welds were investigated with three kinds of welding consumables having different boron (B) and manganese (Mn) contents for high strength carbon steel. The hot crack resistance, measured from self-restraint testing, strongly depended on the amount of B in..... More

Casting/Solidification/Heat Treatment

Abstract
As a first step to optimizing the homogenization heat treatment following high temperature upset forging, the solidification segregation and the homogenization behaviors of solute elements were quantitatively analyzed for 1Cr-1.25Mo-0.25V steel ingot by electron probe micro-analysis (EPMA). The random sampling approach, which was designed to generate continuous compositional profiles of..... More