Microstructure and Mechanical Properties of Continuous Welded 50N Rail
Wookjin Choi1, Min Ji Song1, Nam-Hyoung Lim2, Soo Yeol Lee1
1Department of Materials Science and Engineering, Chungnam National University, Daejeon 34134, Republic of Korea
2Department of Civil Engineering, Chungnam National University, Daejeon 34134, Republic of Korea
Correspondence  Soo Yeol Lee ,Tel: +82-42-821-6637, Email: sylee2012@cnu.ac.kr
  Published online: 30 November 1999.
Rails are subjected to repeated stresses due to wheel-rail contact during train service. Rails under stress conditions undergo microstructural changes, and these cause degradations of the structural integrity and lifetime of rails. In this study, three different rails (newly-manufactured rail, newly-manufactured head-hardened rail, and worn (used) rail) were compared to examine the effects of heat treatment and repeated wheel-rail contact stress on the microstructure and mechanical behavior of continuous welded rail. The crystal structure, constituent phase distribution, tensile property, and hardness were investigated at various locations along a cross section of the rails. All three rails consisted of a mixture of BCC and FCC crystal structures as a majority phase with a very small amount of cementite (Fe3C) as a minor phase. Rietveld analysis revealed that the weighted fractions of the BCC crystal structure were approximately 74%, 64%, and 85% for the new rail, head-hardened rail, and worn rail, respectively. While the web and foot areas of the three rails showed no significant differences in mechanical properties, the railheads of the three rails revealed much higher yield strength, tensile strength, and hardness. The highest tensile strength and hardness were measured at the railhead in the head-hardened rail, and were attributed to the evolution of the bainite phase, generated by additional heat treatment. The higher mechanical strength of the railhead of the worn rail is thought to have resulted from a combination of work hardening and smaller lamellar spacing of the pearlite phase, induced by repeated wear processes during train operation.
Keywords: continuous welded rail, microstructure, mechanical property, X-ray diffraction, crystal structure
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-2-557-1071   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials.                 Developed in M2PI